Lead(II) iodide

Preparation

is commonly synthesized via a precipitation reaction between iodide and lead(II) 2 in water solution:

:

The lead iodide is nearly insoluble at room temperature, and thus precipitates out.

Other soluble compounds containing lead(II) and iodide can be used instead, for example lead(II) acetate and sodium iodide.

The compound can also be synthesized by reacting iodine vapor with molten lead between 500 and 700 °C.

A thin film of can also be prepared by depositing a film of lead sulfide and exposing it to iodine vapor, by the reaction

:

The sulfur is then washed with dimethyl sulfoxide.

Crystallization

Lead iodide prepared from cold solutions usually consists of many small hexagonal platelets, giving the yellow precipitate a silky appearance. Larger crystals can be obtained by exploiting the fact that solubility of lead iodide in water (like those of lead chloride and lead bromide) increases dramatically with temperature. The compound is colorless when dissolved in hot water, but crystallizes on cooling as thin but visibly larger bright yellow flakes, that settle slowly through the liquid — a visual effect often described as "golden rain". Larger crystals can be obtained by autoclaving the with water under pressure at 200 °C.

Even larger crystals can be obtained by slowing down the common reaction. A simple setup is to submerge two beakers containing the concentrated reactants in a larger container of water, taking care to avoid currents. As the two substances diffuse through the water and meet, they slowly react and deposit the iodide in the space between the beakers.

Another similar method is to react the two substances in a gel medium, that slows down the diffusion and supports the growing crystal away from the container's walls. Patel and Rao have used this method to grow crystals up to 30 mm in diameter and 2 mm thick.

The reaction can be slowed also by separating the two reagents with a permeable membrane. This approach, with a cellulose membrane, was used in September 1988 to study the growth of crystals in zero gravity, in an experiment flown on the Space Shuttle Discovery.

can also be crystallized from powder by sublimation at 390 °C, in near vacuum or in a current of argon with some hydrogen.

Large high-purity crystals can be obtained by zone melting or by the Bridgman–Stockbarger technique. These processes can remove various impurities from commercial .

Applications

Lead iodide is a precursor material in the fabrication of highly efficient Perovskite solar cell. Typically, a solution of in an organic solvent, such as dimethylformamide or dimethylsulfoxide, is applied over a titanium dioxide layer by spin coating. The layer is then treated with a solution of methylammonium iodide and annealed, turning it into the double salt methylammonium lead iodide , with a perovskite structure. The reaction changes the film's color from yellow to light brown.

is also used as a high-energy photon detector for gamma-rays and X-rays, due to its wide band gap which ensures low noise operation.

Lead iodide was formerly used as a paint pigment under the name "iodine yellow". It was described by Prosper Mérimée (1830) as "not yet much known in commerce, is as bright as orpiment or chromate of lead. It is thought to be more permanent; but time only can prove its pretension to so essential a quality. It is prepared by precipitating a solution of acetate or nitrate of lead, with potassium iodide: the nitrate produces a more brilliant yellow color." However, due to the toxicity and instability of the compound it is no longer used as such. It may still be used in art for bronzing and in gold-like mosaic tiles.

Stability

Common material characterization techniques such as electron microscopy can damage samples of lead(II) iodide. Thin films of lead(II) iodide are unstable in ambient air. Ambient air oxygen oxidizes iodide into elemental iodine:

:

Toxicity

Lead iodide is very toxic to human health. Ingestion will cause many acute and chronic consequences characteristic of lead poisoning. Lead iodide is an inhalation hazard, and appropriate respirators should be used when handling powders of lead iodide.

Structure

The structure of , as determined by X-ray powder diffraction, is primarily hexagonal close-packed system with alternating between layers of lead atoms and iodide atoms, with largely ionic bonding. Weak van der Waals interactions have been observed between lead–iodide layers.

|File:Lead (II) iodide precipitating out of solution.JPG|Lead(II) iodide precipitates when solutions of potassium iodide and lead(II) nitrate are combined |File:Iodide lead(II).jpg|Experiment "golden rain" where iodide of lead(II) was recrystallized from hot solution by cooling, forming crystals of golden-yellow

References

Cited sources

References

1. (1980). "The Solubility of Some Sparingly Soluble Lead Salts: An Evaluation of the Solubility in Water and Aqueous Electrolyte Solution". J. Phys. Chem..
2. (2002). "Electronic and optical properties of lead iodide". Journal of Applied Physics.
3. (2017). "Large-scale 2D PbI₂ monolayers: experimental realization and their indirect band-gap related properties". Nanoscale.
4. (1981). "X-ray study of the PbCl_2−xI_x and PbBr_2−xI_x systems". Journal of Solid State Chemistry.
5. Forty, A. J.. (August 1960). "Observations of the decomposition of crystals of lead iodide in the electron microscope". Philosophical Magazine.
6. (2019-02-12). "Atomic Layer Deposition of PbI₂ Thin Films". Chemistry of Materials.
7. "Haz-Map Category Details".
8. (1979). "Polytypism and the vibrational properties of I₂". Physical Review B.
9. (2012). "Fabrication of excitonic luminescent inorganic{{nbhyph}}organic hybrid nano and microcrystals". [[The Optical Society.
10. (1990). "Synthesis and characterization of lead(II) iodide grown in space". Chemistry of Materials.
11. (2015). "Removal of oxidic impurities for the growth of high purity lead iodide single crystals". Journal of Crystal Growth.
12. (1982). "Preparation of lead iodide films by iodination of chemically deposited lead sulphide films". Materials Research Bulletin.
13. (2016). "Composition and crystal structure of perovskite films attained from electrodes of used car battery".
14. (2004). "The Pigment Compendium: a Dictionary of Historical Pigments". Butterworth-Heinemann.
15. (2012). "Toxicity of lead: a review with recent updates". Interdisciplinary Toxicology.
16. (2015). "Whispering Gallery Mode Lasing from Hexagonal Shaped Layered Lead Iodide Crystals". ACS Nano.
17. (1952). "The extraction of lead iodide by methyl iso-propyl ketone". Analytica Chimica Acta.
18. "Sigma-Aldrich catalog: Lead(II) iodide 99%".
19. (2009). "Study of the influence of the rare-earth elements on the properties of lead iodide". Journal of Crystal Growth.
20. Fleming, Declan. (6 January 2015). "Golden rain". [[Education in Chemistry]].
21. Anthony, Seth. (2014). "I. Cognitive and instructional factors relating to students' development of personal models of chemical systems in the general chemistry laboratory. [...]". Colorado State University.
22. Patnaik, P.. (2002). "Handbook of Inorganic Chemicals". McGraw-Hill.
23. (2016). "Facile growth and characterization of freestanding single crystal PbI₂ film". Materials Letters.
24. "Lead iodide film".
25. (1934). "Preparation of crystals of sparingly soluble salts". Journal of Chemical Education.
26. (1980). "An improved design to grow larger and more perfect single crystals in gels". Journal of Crystal Growth.
27. (2001). "Lead iodide film deposition and characterization". Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment.
28. (1996). "Lead iodide x-ray detection systems". Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment.