7075 aluminium alloy

Basic properties

Aluminium 7075A has a density of 2.810 g/cm3.

Mechanical properties

The mechanical properties of 7075 depend greatly on the tempering of the material.

Aluminum 7075 has a low formability at low room temperature and is vulnerable to stress corrosion cracking. Using different elevated temperature forming techniques has been shown to reduce springback and fracture. Examples of those elevated temperature forming techniques are retrogression forming and warm forming.

7075-O

Un-heat-treated 7075 (7075-0 temper) has a maximum tensile strength of no more than 40000 psi, and maximum yield strength of no more than 21000 psi. The material has an elongation (stretch before ultimate failure) of 9–10%. As is the case for all 7075 aluminum alloys, 7075-0 is highly corrosion-resistant combined with generally acceptable strength profile.

7075-T6

T6 temper 7075 has an ultimate tensile strength of 74000 - and yield strength of at least 63000 -. It has a failure elongation of 5–11%.

The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours. This yields the peak strength of the 7075 alloys. The strength is derived mainly from finely dispersed eta and eta' precipitates both within grains and along grain boundaries.

7075-T651

T651 temper 7075 has an ultimate tensile strength of 83000 psi and yield strength of 73000 psi. It has a failure elongation of 3–9%. These properties can change depending on the form of material used. The thicker plates may exhibit lower strengths and elongation than the numbers listed above.

7075-T7

T7 temper has an ultimate tensile strength of 505 MPa and a yield strength of 435 MPa. It has a failure elongation of 13%. T7 temper is achieved by overaging (meaning aging past the peak hardness) the material. This is often accomplished by aging at 100–120 °C for several hours and then at 160–180 °C for 24 hours or more. The T7 temper produces a microstructure of mostly eta precipitates. In contrast to the T6 temper, these eta particles are much larger and prefer growth along the grain boundaries. This reduces the susceptibility to stress corrosion cracking. T7 temper is equivalent to T73 temper.

7075-RRA

The retrogression and reage (RRA) temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper, it involves overaging past peak hardness (T6 temper) to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels.

RRA treatments can be accomplished with many different procedures. The general guidelines are retrogressing between 180 and 240 °C for 15 min 10 s.

Equivalent materials

Uses

The world's first mass-production usage of the 7075 aluminum alloy was for the Mitsubishi A6M Zero fighter. The aircraft was known for its excellent maneuverability which was facilitated by the higher strength of 7075 compared to previous aluminum alloys.

7000 series alloys such as 7075 are often used in transport applications due to their high specific strength, including marine, automotive and aviation. These same properties lead to its use in rock climbing equipment, bicycle components, inline-skating-frames and hang glider airframes are commonly made from 7075 aluminium alloy. Hobby-grade RC models commonly use 7075 and 6061 for chassis plates. 7075 is used in the manufacturing of M16 rifles for the U.S. military as well as AR-15 style rifles for the civilian market. In particular high-quality M16 rifle lower and upper receivers, as well as extension tubes, are typically made from 7075-T6 alloy. Desert Tactical Arms, SIG Sauer, and French armament company PGM use it for their precision rifles. It is also commonly used in shafts for lacrosse sticks, such as the STX sabre, and camping knife and fork sets. It is a common material used in competition yo-yos as well.

Another application for the 7075-series alloy has been in connecting rods used in drag racing engines. Aluminum rods do not have the fatigue life of forged steel rods, but have less mass than their steel counterparts, resulting in lower mechanical stress during periods in which an engine is operated under full-throttle, high-RPM conditions.

It has also been the standard material for crankcase guards on off-road motorcycles.

Due to its high strength, low density, thermal properties, and its ability to be highly polished, 7075 is widely used in mold tool manufacturing. This alloy has been further refined into other 7000 series alloys for this application, namely 7050 and 7020.

Aerospace applications

7075 was used in the Space Shuttle SRB nozzles, and the external tank SRB beam in the Inter-tank section. The forward- and aft skirt as well as the Interstage of the S-II, the second stage of the Saturn V was made from 7075.

Applications

1. Aircraft fittings
2. Gears and shafts
3. Missile parts
4. Regulating valve parts
5. Worm gears
6. Aerospace/defense applications
7. Automotive
8. Bicycle Chainrings
9. Bicycle Gearboxes
10. Archery equipment

Trade names

7075 has been sold under various trade names including Zicral/Zycral, Ergal, and Fortal Constructal. Some 7000 series alloys sold under brand names for making molds include Alumec 79, Alumec 89, Contal, Certal, Alumould, and Hokotol.

References

References

1. [https://materialsdata.nist.gov/bitstream/handle/11115/166/Thermophysical%20Properties.pdf?isAllowed=y&sequence=3 Juan J. Valencia, Peter N. Quested, "Thermophysical Properties"]
2. ASM Handbook Volume 2: Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, 1990 pp. 137–38
3. Yoshio, Baba.[https://www.jstage.jst.go.jp/article/jilm1951/39/5/39_5_378/_article/cited-by "Extra super duralumin and successive aluminium alloys for aircraft."] ''Journal of Japan Institute of Light Metals (Sumitomo Light Metal Ind. Ltd., Japan)'' (in Japanese), Volume 39, Issue 5, p. 378. Retrieved: 22 November 2015.
4. Yoshida, Hideo. (February 1, 2023). "History of the Development of Extra Super Duralumin and Future Research Issues of Al–Zn–Mg Alloys". Materials Transactions.
5. Canadian Aeronautics and Space Journal, 1989 vol 35-36 p. 129
6. "7075 (AlZn5.5MgCu, 3.4365, 2L95, A97075) Aluminum :: MakeItFrom.com".
7. [http://www.alcoa.com/mill_products/catalog/pdf/alloy7075techsheet.pdf Alcoa 7075 data sheet] {{Webarchive. link. (2013-08-29 (PDF), accessed October 13, 2006)
8. Ogunsanya, Ibrahim G.. (2024). "Corrosion and hardness properties of retrogression-formed and warm-formed AA7075 sheet". Engineering Reports.
9. "ASM Material Data Sheet".
10. Park, J. K., and A. J. Ardell. "Microstructures of the Commercial 7075 AI Alloy in the T651 and T7 Tempers". ''Metall. Trans. A.'' 14A (1983): 1957. Print.
11. "ASM Material Data Sheet".
12. [https://patents.google.com/patent/US3856584 Cina, Baruch M. REDUCING THE SUSCEPTIBILITY OF ALLOYS, PARTICULARLY ALUMINIUM ALLOYS, TO STRESS CORROSION CRACKING]. Israel Aircraft Industries Ltd., assignee. Patent 3856584. 24 Dec. 1974. Print.
13. "7075 Aluminum Alloy Properties, 7075-T6, T7351, T651".
14. Yoshida, Hideo (2020). Shoeisha. {{ISBN. 978-4-86693-295-8
15. T Hashimoto, S Jyogan (Showa Aluminium), K Nakata, Y G Kin and M Ushio (Osaka University): FSW joining of high strength Al alloy
16. McCutcheon, Kimble D.. (3 August 2022). "U.S. Manned Rocket Propulsion Evolution Part 8.20: The Saturn V S-II".